PROPERTY | UNIT | VALUE / RANGE |
Melting Point | °C | 430 - 435 |
Density | g mL-1 | 1.38 |
Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 1.5 - 1.8 |
Thermal Conductivity | W / mK | |
PROPERTY | UNIT | VALUE / RANGE |
Tensile Strength, Yield at 23 C | MPa | |
Tensile Strength, Break at 23 C | MPa | 590 - 860 |
Elongation, Yield | % | |
Elongation, Break | % | 20 - 45 |
Tensile Modulus at 23 C | MPa | 7800 - 12100 |
Flexural Strength, Yield | MPa | |
Flexural Modulus | MPa |
PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | 5 · 10-16 | |
Dielectric Strength | V/mm x 104 | 1.7 - 3.3 | |
Dielectric Constant @ 60 Hz | n/a | 1.6 - 3.7 | |
Dissipation Factor @ 60 Hz | n/a | 0.004 - 0.007 |
PROPERTY | UNIT | VALUE / RANGE | |
| °C | ||
Water Absorption, 24 hr. Immersion | % | 5.0 - 9.0 |